Microstructure and wear properties of TiCN/Ti coatings on titanium alloy by laser cladding

Titanium carbide nitride (TiCN) reinforced Ti coating was fabricated on the surface of Ti–6Al–4V alloy by laser cladding method. Microstructure and wear properties at the surface of the coating in atmosphere were investigated. Three zones can be distinguished of the coating: the clad zone (CZ), the heat affected zone (HAZ) and the substrate. The clad zone is composed of TiCN dendrites, TiO2 and Ti. A metallurgical bonding between the coating and the substrate was obtained. The microhardness and wear resistance of the TiCN/Ti coating are significantly improved. The average hardness of the coating is about 3 to 6 times of that of the substrate. The friction coefficients of the substrate and the coating are 0.48 and 0.34 respectively. The friction coefficient of the Ti–6Al–4V substrate was insensitive to the normal load, while that of the cladded TiCN/Ti coating was very sensitive to the normal load. The wear mass losses of the cladded samples are much lower than that of the substrate whatever the normal load is.