Failure analysis of the flash evaporator in an alumina production plant

• The failure cause of a flash evaporator was investigated.
• Uniform corrosion was not the main cause.
• Many branch cracks which propagated intergranularly were observed.
• Failure of the flash evaporator was caused by caustic embrittlement.
• The necessary conditions for caustic embrittlement were satisfied.