The effect of post surface silanization and luting agents on the push-out bond strengths of adhesively inserted fiber reinforced posts

The effect of silane treatment on the push-out bond strengths of three different luting agents to fiber-reinforced composite (FRC) posts after thermocycling was evaluated.Sixty single-rooted human maxillary central incisors were sectioned below the cemento–enamel junction, and the roots were endodontically treated. RelyX Fiber Posts (size #2) were inserted using etch-and-rinse, self-etch, and self-adhesive luting agents (cementing agents). For half of the specimen in each group, the fiber posts were treated with a silane coupling agent. Bonded specimens were cut (2-mm-thick sections) and push-out tests were performed (crosshead speed, 0.5 mm/min). Failure modes were evaluated using a stereomicroscope at original magnification ×40.For each luting agent the use of silane did not result in any statistically significant difference at any level of the root compared to those of the control groups except for Variolink II and RelyX Unicem luting agents in apical root section (p<0.05; one-way ANOVA). The post hoc analysis showed that regardless of the pre-treatment procedures, Variolink II achieved significantly higher bond strengths than Panavia F 2.0 and RelyX Unicem in all root sections (p<0.05).The use of a silane coupling agent had no influence on bond strengths depending on the luting agent used, whereas the type of luting agent (etch-and-rinse, self-etch, and self-adhesive) appeared to be a significant influence on the push-out bond strength values independent of the pre-treatment used. Therefore, pre-treatment of fiber posts with a silane coupling agent does not seem to be mandatory, which saves time in the clinical situation.