Interaction of corrosion defects in pipelines – Part 2: MTI JIP database of corroded pipe tests
چکیده انگلیسی

Corrosion defects, also called metal loss due to corrosion, are frequently found in carbon steel pipelines. Corrosion defects may occur singly or in colonies. Usually the failure pressure of a colony of closely spaced corrosion defects is smaller than the failure pressures that the defects would attain if they were isolated. This reduction in the corroded pipe pressure strength is due to the interaction between adjacent defects. The interaction of corrosion defects in pipelines is the subject of two companion papers. In the preceding paper (the Part 1 paper) a literature review and the fundamentals of interaction of corrosion defects in pipelines were presented. In the present paper (the Part 2 paper) initially the database of corroded pipe tests generated during the MTI JIP is described. Then the failure pressures contained in the MTI JIP database of corroded pipe tests are compared with those predicted by six of the currently available assessment methods. MTI JIP is the acronym for Mixed Type Interaction Joint Industry Project.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: International Journal of Pressure Vessels and Piping - Volume 145, September 2016, Pages 41–59
نویسندگان
, , , ,