![عکس صفحه اول مقاله: Effect of vibration loading on the fatigue life of part-through notched pipe Effect of vibration loading on the fatigue life of part-through notched pipe](/preview/png/787441.png)
A systematic experimental and analytical study has been carried out to investigate the effect of vibration loading on the fatigue life of the piping components. Three Point bend (TPB) specimens machined from the actual pipe have been used for the evaluation of Paris constants by carrying out the experiments under vibration + cyclic and cyclic loading as per the ASTM Standard E647. These constants have been used for the prediction of the fatigue life of the pipe having part-through notch of a/t = 0.25 and aspect ratio (2c/a) of 10. Predicted results have shown the reduction in fatigue life of the notched pipe subjected to vibration + cyclic loading by 50% compared to that of cyclic loading. Predicted results have been validated by carrying out the full-scale pipe (with part-through notch) tests. Notched pipes were subjected to loading conditions such that the initial stress-intensity factor remains same as that of TPB specimen. Experimental results of the full-scale pipe tests under vibration + cyclic loading has shown the reduction in fatigue life by 70% compared to that of cyclic loading. Fractographic examination of the fracture surface of the tested specimens subjected to vibration + cyclic loading have shown higher presence of brittle phases such as martensite (in the form of isolated planar facets) and secondary micro cracks. This could be the reason for the reduction of fatigue life in pipe subjected to vibration + cyclic loading.
► Vibration loading affects fatigue crack growth rate.
► Crack initiation life depends on crack tip radius.
► Crack initiation life depends on the characteristic distance.
► Characteristic distance depends on the loading conditions.
► Vibration + cyclic load gives lower fatigue life.
Journal: International Journal of Pressure Vessels and Piping - Volume 88, Issue 10, October 2011, Pages 415–422