An experimental study of inhomogeneous cyclic plastic deformation of 1045 steel under multiaxial cyclic loading

An experimental study was conducted on the inhomogeneous cyclic plastic deformation of 1045 steel under multiaxial cyclic loading. Thin-walled tubular specimens were used and small strain gages were bonded on the specimen surface to characterize the local deformation. The controlled loading paths included cyclic tension–compression, cyclic torsion, proportional axial-torsion, 90°-out-of-phase axial-torsion, and fully reversed torsion with a constant axial stress. The maximum stress in each experiment was lower than the lower yield stress of the material. It was found that the cyclic plastic deformation within the gage section of the specimen under multiaxial stress state followed the three-stage process that was observed from uniaxial loading, namely, incubation, propagation, and saturation. The plastic deformation was significantly inhomogeneous during the propagation stage, and the inhomogeneity continued through the saturation stage. The duration of each stage and the saturated strains were dependent on the cyclic stress amplitude and the loading path. Multiaxial stress state reduced the incubation stage. With identical equivalent stress magnitude, the nonproportional loading path resulted in the shortest incubation and propagation stages, and the saturated equivalent plastic strain magnitude was the smallest. Although the deformation over the gage section was inhomogeneous, the plastic deformation in a given local area was found to be practically isotropic.