Wear behaviour of thermal flame sprayed FeCr coatings on plain carbon steel substrate

The principle aim of this study is to investigate the wear behaviour of FeCr coatings on Ni-based bond deposited plain carbon steel substrate for several applications in power generation plants. For this purpose, FeCr and Ni-based powders were sprayed on plain carbon steel substrates using a thermal flame spray technique. Fabricated layers were characterized by using a X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), microhardness and surface roughness testers. FeCr coatings were subjected to sliding wear against AISI 303 stainless steel counter bodies under dry and acidic environments. A pin-on-plate type of apparatus was used with normal loads of 49 and 101 N and sliding speed of 1 Hz. XRD results revealed that FeCr, Fe, Cr, Fe–Cr–Ni, γ-Fe2O3 and Fe3O4 phases are exist in the coating. In addition, some inhomogenities such as oxides, porosity, cracks, unmelted particles and inclusions were observed by SEM. The surface morphologies of FeCr samples after wear experiments were examined by SEM and EDS. It was found that friction coefficients of the coatings in dry condition are higher than that in acidic environment.