Comparison of anodised aluminium surfaces from four fabrication methods

This study presents a comparative analysis of surface characteristics and properties of anodised aluminium cylinders produced by sand casting, permanent mould casting, extrusion, and high pressure die casting. Differences in micro structure and distribution of silicon particles in the aluminium, due to the fabrication method and the silicon content in the alloy, resulted in varying thickness of the oxide layers (mean thicknesses between 7 and 19 μm) and surface topography. The oxide layer was unevenly thick for the permanent mould cast and the sand cast cylinders, resulting in a surface with higher plateaus and lower areas. This was more prominent for the sand cast surface. The oxide of the extruded cylinder was thick and even and its surface was smooth. The high pressure die cast surface had an oxide that was very thin and uneven. The surfaces displayed different results in the scratch test due to the variations in the surface structure. For the permanent mould cast and the sand cast surfaces the silicon particles present in the oxide deflected the cracks that were formed during the scratching. This resulted in smaller wear debris. The nanohardness values of the oxides had a large scattering due to the inhomogeneous nature of the oxide layers, with pores and particles. However, the highest nanohardness values were between 5000 and 6000 MPa for the four surfaces, which is significantly lower than that of sintered alumina. In the micro abrasion test the wear mechanism for all four surfaces was microcutting resulting in chippings.

► We investigate four anodised aluminium surfaces from different fabrication methods.
► Fabrication methods: extrusion, permanent mould-, sand-, high pressure die casting.
► Different surface topography and oxide structure due to fabrication method.
► Different cracking behaviour during scratching due to surface structure variations.
► Similar nanohardness and micro abrasion wear mechanisms.