Microstructure and mechanical properties of mechanically alloyed ODS copper alloy for fusion material application
ترجمه فارسی عنوان
ریزساختار و خواص مکانیکی آلیاژ آلومینیوم آلیاژ آلومینیوم آلیاژ آلومینیوم برای کاربرد مواد فیوژن
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی انرژی
انرژی هسته ای و مهندسی
چکیده انگلیسی
Advanced oxide dispersion strengthened copper alloys are promising structural materials for application in divertor system of future fusion reactors due to high irradiation resistance, high thermal conductivity, and good mechanical properties. In this study, a new ODS copper including 0.42wt%Y2O3 nanosized oxide particles was developed successfully by mechanical alloying method using addition of 1 wt% Stearic acid in Ar atmosphere. Mechanical alloying resulted in decrease of crystallite size to 28â¯nm in concurrent with increment of dislocation density and hardness to the saturated level of 1.7Ã1015mâ2 and 226HV0.1 after 48 h milling, respectively. Consolidated ODS copper by SPS and then hot roll-annealing at 900°C/60â¯min showed an average grain size of 1.1â¯Âµm with a near random texture. Furthermore, TEM observations demonstrated fine semicoherent Y2O3 oxide particles distributed with a misfit parameter (δ) of 0.17 in copper matrix with an average size of 10.8â¯nm and interparticle spacing of 152â¯nm. Finally, tensile test evaluation determined comparable mechanical properties of the annealed ODS copper (Cu-0.42wt%Y2O3) with Glidcop-Al25 including a yield strength of 272â¯MPa and total elongation of 12%, by two mechanisms of grain boundary strengthening and oxide particle strengthening.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Nuclear Materials and Energy - Volume 15, May 2018, Pages 17-22
Journal: Nuclear Materials and Energy - Volume 15, May 2018, Pages 17-22
نویسندگان
S.M.S. Aghamiri, N. Oono, S. Ukai, R. Kasada, H. Noto, Y. Hishinuma, T. Muroga,