Microstructure of fatigue-tested F82H steel under multi-axial loadings

Sudden cyclic softening results from the formation of mobile dislocations in grain interiors during the initial stage of loading. The significant reduction in the lifetime is directly correlated with the high density of dislocations generated during circle loadings.