Magnetic properties and thermal stability of Ti-doped CrO2 films

Chromium dioxide (CrO2) is a striking half metal material which may have important applications in the field of spintronics. However, pure CrO2 film is metastable at room temperature and the synthesis process can be only performed in a narrow temperature range of 390-410 °C with TiO2 used as substrate material. Here, we report the preparation and investigation of (1 0 0) oriented Ti-doped CrO2 films on TiO2 substrates. It is found that Ti-doped films can maintain pure rutile phase even after a 510 °C post-annealing, showing much better thermal stability than pure CrO2 films. Ti-doped films can be prepared in a wider temperature window (390-470 °C), which may be attributed to the improvement of thermal stability. The broadening of process window may be beneficial for further improvement of film quality by optimizing growth temperature in a larger range. In addition to the improvement of thermal stability, the magnetic properties of Ti-doped CrO2 are also found to be tuned by Ti doping: saturation magnetizations of Ti-doped films at room temperature are significantly lower, and magnetic anisotropy decreases as the Ti-concentration increases, which is beneficial for decreasing switching current density in STT-based spintronic devices.