The effect of Bi substitution on the microstructure and magnetic properties of the Sr0.4Ba0.3La0.3Fe12−xBixO19 hexagonal ferrites

Bi3+ ions doped M-type hexaferrites, Sr0.4Ba0.3La0.3Fe12−xBixO19 (0≤x≤0.7), were prepared by the ceramic process. The phase components of the magnetic powders were investigated by X-ray diffraction. The results show that a single magnetoplumbite phase is obtained for the magnetic powders with x from 0 to 0.2, and BiFeO3 as a second phase appears when Bi content (x)≥0.3. The micrographs of the sintered magnets were observed by a field emission scanning electron microscopy. The sintered magnets are formed of hexagonal-shaped crystals. The magnetic properties of the sintered magnets were measured at room temperature by a permanent magnetic measuring system. The remanence (Br) first increases with x from 0 to 0.2, and then decreases when Bi content (x)≥0.2. The intrinsic coercivity (Hcj) and magnetic induction coercivity (Hcb) firstly decrease quickly with x from 0 to 0.1, and then increase linearly when Bi content (x)≥0.1. The maximum energy product [(BH)max] increases with x from 0 to 0.3, and then decreases when Bi content (x)≥0.3. The ratio Hk/Hcj ratio first increases with Bi content (x) from 0 to 0.4. And the Hk/Hcj ratio decreases when x≥0.4.