Nano-enhanced composite materials under thermal shock and environmental degradation: A durability study

Carbon nanotubes (CNTs) were incorporated at 0.5 wt% in epoxy resin using sonication at two different levels of amplitude (50% and 100% of 400 W nominal sonication power). The CNTs modified epoxy systems were used to manufacture carbon fibre reinforced laminates (CFRPs). All specimens were subjected to thermal shock and hygrothermal exposure. The presence of CNTs did not alter the water absorption profiles for the epoxy resin, but it resulted in a spectacular 40% reduction in the water uptake at equilibrium for the CFRPs. The interlaminar shear strength of the CFRPs was not significantly affected by the thermal shock cycles; however it was reduced by 50–60% after hygrothermal exposure. The addition of CNTs led to slightly lower interlaminar shear strength values in the as-manufactured state. However their presence did not accelerate the deterioration of the strength after the environmental exposure. Although the addition of CNTs did not significantly influence the thermomechanical properties of the resin, they were beneficial in the case of the CFRPs since (i) they enhanced the storage modulus and glass transition temperature and (ii) limited the deterioration of these properties after thermal shock and hygrothermal exposure. The amplitude level during sonication which determined the dispersion state and length of the CNTs had a clear effect on the durability of the studied systems.