Dispersion and roles of montmorillonite on structural, flammability, thermal and mechanical behaviours of electron beam irradiated flame retarded nanocomposite

In this work, the effects of montmorillonite (MMT) dispersion and electron beam irradiation on intercalation and flammability-thermal behaviours of alumina trihydrate (ATH) added low density polyethylene and ethylene vinyl acetate (LDPE–EVA) blends were investigated. MMT and ATH added LDPE–EVA blends were compounded using Brabender mixer and compression moulded into sheets. The samples sheets were electron beam irradiated in the dosage range of 0 to 250 kGy. The dispersion and intercalation of nano-MMT in LDPE–EVA matrix were investigated through X-ray diffraction (XRD) analysis. The d-spacing measurements revealed that the addition of nano-MMT has effectively intercalated into polymer matrix and this has enhanced the compatibility of ATH particles and LDPE–EVA matrix. Limiting oxygen index test (LOI) revealed that the incorporation of MMT into ATH added LDPE–EVA blends as improved the flame retardancy up to 26.5 LOI%. Besides, the application of electron beam irradiation were also improved the flame retardancy of the blends by increasing the LOI% for about 2% compared to non-irradiated samples. The application of irradiation dosage up to 250 kGy has rapidly improved the thermal stability of blends by delaying decomposition temperature and also promoting formation of char. The increasing of MMT loading level and irradiation dosage has effectively enhanced tensile strength and Young’s modulus by intercalating polymer matrix into interlayer galleries of MMT particles. Beside, the formation of crosslinking networks in polymer matrix also could further enhance the tensile strength and Young’s modulus. The intercalation effect of MMT particles and formation of crosslinking networks in polymer matrix could improve the thermal and mechanical properties. Consequently, this study has demonstrated that addition of MMT and electron beam irradiation into ATH added LDPE–EVA blends could produce better flammability, thermal and physical properties of ATH added LDPE–EVA blends.