The SiC/SiCwf laminate design has been targeted to achieve increased residual compressive stress in thin SiCwf layers and small residual tensile stress in thick SiC layers, that would lead to a significant increase of the apparent fracture toughness of the composite. The laminates have been manufactured using rolling and hot pressing techniques. The measured apparent fracture toughness of laminates showed a significant increase over the monolith SiC ceramics. Thus, while the intrinsic fracture toughness of pure SiC ceramics is in the range of 2–3 MPa m1/2, significant increase up to 6–8 MPa m1/2 was achieved for the layered ceramics. A crack shielding by compressive residual stress was a main mechanism responsible for the significant toughening of the SiC/SiCwf laminate.
Journal: Composites Part B: Engineering - Volume 37, Issue 6, 2006, Pages 524–529