Angular dependence of switching behaviour in template released isolated NiFe nanowires

In this article, the magnetisation behaviour and magnetisation reversal process of both single and bundles of 3 and 7 closely-packed template released Ni60Fe40 nanowires were investigated using high-sensitivity Magneto-Optical Kerr Effect (MOKE) magnetometry. The nanowires were deposited from a dilute suspension onto gold pre-patterned silicon substrates. They were typically 9 μm in length with a diameter of approximately 200 nm. By increasing the number of clumped wires a reduction in the switching field was observed, suggesting that overall the bundle behaves like a single system and decreasing the effective external field required to switch the magnetisation. Square hysteresis loops with a sharp jump in the Kerr signal were seen for all MOKE measurement angles. This result may reflect the surface magnetisation of the nanowire, compared to their bulk behaviour as compared with the literature that adopted the same and different investigative techniques on comparable compositions and dimensions of wires. The influence of applying the magnetic field at different angles with respect to the long axis of the nanowire on the switching behaviour was analysed and compared with the theoretical calculations of non-uniform rotation of the curling model of domain reversal. An agreement and disagreement with this model was seen, respectively, for low and high angles, indicating the complexity of the magnetic state of such isolated nanowires. To confirm the results presented here, further studies are recommended using a combination of techniques sensitive to surface and bulk magnetisation on similar isolated ferromagnetic nanowires.