Synthesis, characterization and application of Co doped TiO2 multilayer thin films

To use the visible portion of solar light, 2% cobalt doped TiO2 (Co: TiO2) multilayer thin films having 1, 2, 3 and 4 stacked layers have been deposited on FTO substrates using spray pyrolysis technique. XRD results show that 1 and 2 layers of films have anatase phase. Brookite phase has been appeared at the 3 and 4 layered films. The average grain size of 1, 2, 3 and 4 layers of films are 14.4, 23.5, 29.7 and 33.6 nm respectively. UV-Vis results show that 4th layer film has high absorption in the visible region. The calculated Eg of 1, 2, 3 and 4 layers is 3.54, 3.42, 3.30 and 3.03 eV respectively. The calculated average sheet resistivity of 1, 2, 3 and 4 layers of films is 7.68 × 104, 4.54 × 104, 8.85 × 103 and 7.95 × 102 (ohm-m) respectively, according to four point probe technique. Solar simulator results show that highest solar conversion efficiency (5.6%) has been obtained by using 3 stacked layers photoanode. This new structure in the form of stack layers provides a way to improve the efficiency of optoelectronic devices.