Study on plastic deformation behavior of hot splitting spinning of TA15 titanium alloy

The plastic deformation behavior of hot splitting spinning of TA15 titanium alloy is a complex metal forming problem with multi-factor coupling interactive effects. In this paper, on condition of considering various thermal effects, a three-dimensional (3D) elastic-plastic coupled thermo-mechanical finite element (FE) model of hot splitting spinning of TA15 titanium alloy is established using the dynamic, temp-disp, explicit module of FE software ABAQUS. Based on the analysis of flow behaviors of TA15 titanium alloy, the mechanism and influence of materials plastic deformation behavior during the forming process are studied. The results show that, the flow stress of TA15 titanium alloy generally decreases with the increase of deformation temperature; at the same strain rate, the higher temperature is, the lower flow stress is. The temperature distributions along the circumferential direction of disk blank are even and the temperature of plastic deformation area is about 984 °C. The heat from plastic deformation and friction at local plastic deformation area is less than the dissipated heat, so the temperature just falls into approximately 945 °C. Radial spinning force as the driving force of plastic deformation increases gradually and reaches about 35 kN at the end. The maximum value of equivalent stress is presented in fillet part between disk blank and two mandrels. The distributions of equivalent plastic strain appear the large strain gradients and the obvious characteristics of inhomogeneous deformation. When friction factor on interfaces between disk blank and dies ranges from 0.4 to 0.6, the forming quality and precision are highest.