• Tribological properties of NMSC from RT to 800 °C were tested.
• Tribological properties of NMSC strongly depended on the addition content of WAh.
• WAh and TiC brought about an improvement in tribological properties of NMSC.
• NE showed the excellent tribological properties from RT to 800 °C.
Ni3Al matrix self-lubricating composites (NMSC) containing varied amounts of WS2, Ag and hBN (WAh) with weight ratio of 1:1:1 were fabricated by in situ technique using spark plasma sintering. The friction and wear properties of NMSC against the commercial Si3N4 ceramic ball at the load of 10 N and sliding speed of 0.234 m/s for 80 min from room temperature to 800 °C were investigated. The results showed that the tribological properties of NMSC strongly depended on the addition content of WAh. Moreover, NMSC with 15 wt.% WAh and 5 wt.% TiC exhibited the relatively lower friction coefficients and the less wear rates from RT to 800 °C. The excellent tribological behavior of NMSC with 15 wt.% WAh and 5 wt.% TiC was attributed to the synergetic action of composite lubricants of WAh and reinforced phase of TiC.
Variation of friction coefficients and wear rates of NMSC with temperatures: Ni3Al based alloy (NA), Ni3Al + 10 wt.% WAh (NB), Ni3Al + 15 wt.% WAh (NC) and Ni3Al + 20 wt.% WAh (ND), Ni3Al + 15 wt.% WAh + 5 wt.% TiC (NE).Figure optionsDownload as PowerPoint slide
Journal: Materials & Design - Volume 55, March 2014, Pages 75–84