Effects of solids loading on microstructure and mechanical properties of HfB2–20 vol.% MoSi2 ultra high temperature ceramic composites through aqueous gelcasting route
موضوعات مرتبط
مهندسی و علوم پایه سایر رشته های مهندسی مهندسی (عمومی)
پیش نمایش صفحه اول مقاله
Effects of solids loading on microstructure and mechanical properties of HfB2–20 vol.% MoSi2 ultra high temperature ceramic composites through aqueous gelcasting route
چکیده انگلیسی

HfB2–20 vol.% MoSi2 ultra high temperature ceramic composites were prepared through aqueous gelcasting route. The stability of HfB2 and MoSi2 suspensions were studied by zeta potential measurements, sedimentation tests and apparent viscosity measurements. The solids loading had significant effects on the green and sintered densities, microstructure and mechanical properties of HfB2–MoSi2 composites. The values of flexural strength of the green and sintered bodies ranged from 18.3 to 38.7, and 111.5 to 415.9 MPa, respectively, which were strongly dependent on the solids loading. The values of fracture toughness of the sintered bodies ranged from 2.18 to 4.24 MPa m1/2. The highest relative density, mechanical properties and the most homogeneous microstructure was obtained when the solids loading was 45 vol.%. The highest green strength, flexural strength and fracture toughness were 38.7 ± 5.3 MPa, 415.9 ± 17.0 MPa and 4.24 ± 0.22 MPa m1/2, respectively.


► Stability of HfB2 and MoSi2 in water was studied.
► HfB2–MoSi2 composites were prepared by aqueous gelcasting.
► Solids loading affected the densities, microstructure and mechanical properties.
► The highest mechanical properties were obtained with 45 vol.% solids loading.