Effects of tool rotation speed on microstructures and mechanical properties of AA2219-T6 welded by the external non-rotational shoulder assisted friction stir welding

The external non-rotational shoulder assisted friction stir welding (NRSA-FSW) was applied to weld high strength aluminum alloy 2219-T6 successfully, and effects of the tool rotation speed on microstructures and mechanical properties were investigated in detail. Defect-free joints were obtained in a wide range of tool rotation speeds from 600 rpm to 900 rpm, but cavity defects appeared on the advancing side when the tool rotation speed increased to 1000 rpm. The microstructural deformation and heat generation were dominated by the rotating tool pin and sub-size concave shoulder, while the non-rotational shoulder helped to improve the weld formation. Microstructures and Vickers hardness distributions showed that the NRSA-FSW is beneficial to improving the asymmetry and inhomogeneity, especially in the weld nugget zone (WNZ). At the tool rotation speed of 800 rpm, both the tensile strength and the elongation reached the maximum, and the maximum tensile strength was up to 69.0% of the base material. All defect-free joints were fractured at the weakest region with minimum Vickers hardness in the WNZ, while for the joint with cavity defects the fracture occurred at the defect location.

► The NRSA-FSW is successfully applied to weld the high strength aluminum alloy 2219-T6.
► Defect-free joints can be obtained in a wide range of tool rotation speeds.
► The weld formation is dominated by the tool pin especially at high rotation speeds.
► Fine and equaxied grains in the WNZ are affected by the tool rotation speed greatly.
► All defect-free joints are fractured at the location with minimum Vickers hardness.