Effect of Cu addition on microstructure and mechanical properties of 15%Cr super martensitic stainless steel

The effect of adding different content of Cu (0 wt.%, 1.5 wt.% and 3 wt.%) to the 15%Cr super martensitic stainless steel (SMSS) was investigated using optical microscope, scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD). Its consequence on mechanical properties was examined to clarify the role of Cu in the tested steels. The experimental results indicate that the microstructures of three tested steels are tempered martensite, retained austenite and reversed austenite; two kinds of austenites are dispersedly distributed among martensite matrix. Cu can solute in matrix under quenching condition and can precipitate as Cu-rich nanometer phase (ε-Cu) during tempering. Cu is helpful for the grain refinement and to promote the formation of reversed austenite during tempering. The maximum volume fraction of austenite is 55.9% in the steel with 3 wt.% Cu, which is responsible for the improvement of ductility. The results of the mechanical properties tests reveal that the mechanical properties are significantly influenced by the volume fraction of austenite. Cu can cause solid solution strengthening, precipitation strengthening and grain refinement strengthening in SMSS. Cu alloyed super martensitic stainless steel exhibits greatly improved mechanical properties.

► Cu contributes to refine the grains.
► Cu solutes in matrix under quenching and precipitates as ε-Cu during tempering.
► Cu promotes the kinetics of reversed austenite formation.
► Mechanical properties are significantly influenced by austenite amount.
► Cu alloyed super martensitic stainless steel exhibits greatly improved mechanical properties.