Effect of surface texturing on friction properties of WC/Co cemented carbide

An experimental study was carried out to investigate the tribological properties of different surface textured WC/Co cemented carbide. The influence of applied load, sliding speed and area density of textures on frictional performance of surface textured patterns was investigated by Taguchi method. Results show that the textured surfaces filled with molybdenum disulfide solid lubricants can reduce the average friction coefficient, wear rates of Ti–6Al–4V alloy balls and adhesion of Ti–6Al–4V alloy materials on the worn track of cemented carbide compared with un-textured ones. Variance analysis of the experimental data indicates that the area density of textures plays major contribution of both average friction coefficient and wear rate of Ti–6Al–4V alloy balls. Higher area density of textures is beneficial to improve tribological performance of the cemented carbide samples. Sliding speed seems to have no effect on the tribological performance of textured surfaces within the reliability interval of 90%. Applied load has effect on both average friction coefficient and wear rate of Ti–6Al–4V alloy balls at the reliability interval of 95%.

► Tribological properties of surface textured WC/Co cemented carbide were studied.
► Textured surfaces have better performance of antifriction and antiwear.
► Area density of textures has significant effect on tribological performance.