The dry sliding wear tests were carried out on AISI 316 austenitic stainless steel (ASS) plasma coated with NiCrBSiCFe alloy powder under two set of plasma spraying parameters (PSP-1 and PSP-2). EN 8 medium carbon steel was used as a counterface material. The tests were carried out at loads of 20 N and 40 N with a constant sliding velocity of 1 m/s at room temperature (35°), 150 °C, 250 °C and 350 °C. Metallographic characterisation was carried out by optical microscope (OM), scanning electron microscope (SEM) and X-ray diffraction (XRD). Between the two plasma parameters tested, stand-off distance of 125 mm was found to be more suitable for producing uniform lamellar microstructure with fewer amounts of pores which shows better wear resistance. The wear rate at 250 °C was comparatively more due to the material softening and adhesion by intermolecular bonding. The worn debris collected during sliding at 350 °C turn into oxides which further behaves like a protective and lubricative film eliminating the chances of severe material loss. SEM was used to characterise the worn track and debris to identity the wear mechanism.
► Effect of plasma spraying parameters, especially the stand-off distance.
► Effect of microstructure and applied load on coating in sliding wear.
► The reason for maximum wear rate at 250 °C and the minimum wear at 350 °C were explained.
► The worn debris were characterised by SEM analysis and correlated with wear rate.
Journal: Materials & Design (1980-2015) - Volume 36, April 2012, Pages 141–151