The hot working behavior of 17-4 PH stainless steel (AISI 630) was studied by hot compression test at temperatures of 950–1150 °C with strain rates of 0.001–10 s−1. The progress of dynamic recrystallization (DRX) was modeled by the Johnson–Mehl–Avrami–Kolmogorov (JMAK) kinetics equation. The flow softening was directly related to the DRX volume fraction and the DRX time was determined by strain rate. For quantification of recrystallization rate, the reciprocal of the time corresponding to the DRX fraction of 0.5% or 50% was used. Analysis of the sigmoid-shaped recrystallization curves revealed that the rate of DRX increases with increasing deformation temperature and strain rate. The Zener-Hollomon parameter (Z) was found to be inappropriate for analysis of DRX kinetics. Therefore, the dynamic recrystallization rate parameter (DRXRP) was introduced for this purpose. The DRXRP may be determined readily from the Avrami analysis and can precisely predict the rate of DRX at hot working conditions.
Journal: Materials & Design - Volume 31, Issue 10, December 2010, Pages 4577–4583