Effect of TaC addition on the microstructures and mechanical properties of Ti(C, N)-based cermets

The microstructures of the prepared Ti(C, N)-based cermets with various TaC additions were studied using X-ray diffractometry (XRD) and scanning electron microscopy (SEM). Mechanical properties such as transverse rupture strength (TRS), fracture toughness (K1C) and hardness (HRA) were also measured. The results showed that the grain size of the cermets decreased with increasing TaC addition, but too high TaC addition resulted in agglomeration of the grains. An increasing TaC addition increased the dissolution of tungsten, titanium, molybdenum and tantalum in the binder phase. The hardness of the cermets decreased slightly with increasing TaC addition. The transverse rupture strength was the highest for the cermets with 5 wt.% TaC addition, which was characterized by fine grains, homogeneous microstructure and the moderate thickness of rim phase in the binder. The fracture toughness of the cermets with TaC addition from 0 to 5 wt.% decreased obviously, which resulting from decreased grain size. The further decreasing of fracture toughness for the cermets with 7 wt.% TaC addition was due to increased porosity and interfacial tensile stress.