Compressive and wear properties of bulk nanostructured Al2024 alloy prepared by mechanical milling and hot pressing methods were investigated. Al2024 powders were subjected to high-energy milling for 30 h to produce nanostructured alloy. As-milled powders were compacted at 500 °C under 250 MPa in a uniaxial die. Consolidated sample had an average hardness and relative density values of 207.6 HV and 98%, respectively. Uniaxial compression tests at strain rates in the range of 1.67 × 10−4–1.67 × 10−2 s−1 were performed using an Instron-type machine. The wear behavior of nanostructured sample was investigated using a pin-on-disk technique under an applied load of 20 N. The compression and wear experiments were also executed on samples of commercial coarse-grained Al2024-O (annealed) and Al2024-T6 (artificially-aged) alloys, for comparison. The structure of consolidated Al2024 was characterized by X-ray diffraction (XRD). The yield strength and compressive strength of nanostructured Al2024 reached a value of ∼698 MPa and ∼712 MPa at strain rate of 1.67 × 10−4 s−1, respectively, which was considerably higher than those for coarse-grained Al2024-O and Al2024-T6 counterparts. Worn surfaces and the wear debris were analyzed by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and XRD. Nanostructured Al2024 revealed a low friction coefficient of 0.3 and a wear rate of ∼12 × 10−3 mg/m, which are significantly lower than those obtained for Al2024-O and Al2024-T6 alloys. This enhanced wear resistance was mainly caused by nanocrystalline structure with high hardness value. The dominating wear mechanism of nanostructured Al2024 appeared to be delamination mechanism.
Journal: Materials & Design - Volume 31, Issue 2, February 2010, Pages 663–669