Hot deformation behavior and microstructural evolution of Ag-containing 2519 aluminum alloy

The hot deformation behaviors of Ag-containing 2519 aluminum alloy were studied by isothermal compression at 300–500 °C with strain rates from 0.01 s−1 to 10 s−1. The microstructural evolution of the alloy was investigated using Polyvar-MET optical microscope and Tecnai G2 20 transmission electron microscope (TEM). It has been shown that the flow stress of the alloy increases with increasing the strain rate and decreasing the deformation temperature. When the strain rate is lower than 10 s−1, the flow stress increases with increasing strain until the stress reached the peak value, after which the flow stress remains almost constant. This result indicates that dynamic recovery happens during deformation. When the strain rate is 10 s−1 and the temperature is higher than 300 °C, serrated flow behavior is generally observed with the stress decreasing with increasing strain, a typical phenomenon of dynamic recrystallization.