Characteristic properties of Al–Cu–SiCp and Al–Cu–B4Cp composites produced by hot pressing method under nitrogen atmosphere
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه سایر رشته های مهندسی مهندسی (عمومی)
پیش نمایش صفحه اول مقاله
Characteristic properties of Al–Cu–SiCp and Al–Cu–B4Cp composites produced by hot pressing method under nitrogen atmosphere
چکیده انگلیسی

Hot pressing of powders is more effective consolidation method for producing particulate composites than other producing techniques because of improving wettability which gives sound parts without pores. The aim of this study is to produce composites of Al–Cu–SiCp and Al–Cu–B4Cp by using hot pressing method and investigating their characteristic properties. The volume fractions of the reinforced (SiC, B4C) composites were 10, 20 and 30 (vol%). The composites were treated in solution for 24 h at 530 °C to evaluate heat treatment effect on the composites then aged in oil bath at 180 °C for various ageing periods and hardness reached to a maximum value within 8–10 h using Brinnel hardness (HB) tester. In addition, wear resistance of the aged and unaged composite specimens were also investigated by using a pin-on-disc type apparatus under dry sliding conditions at constant speed using 100, 150 and 220 grade SiC abrasive paper under constant loads of 2, 4, 6, 8 and 10 N at room temperature. As a result, the distribution of the reinforced particle was uniform by examining their microstructures. The hardness and the wear performance of the composite increased with increasing volumetric reinforced particle content. Wear rate increased with 100 grade SiC than 220 SiC grade by additional of the reinforced particulate.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials & Design - Volume 28, Issue 4, 2007, Pages 1238–1244
نویسندگان
,