Weldability of Al4C3–Al composites via diffusion welding technique
موضوعات مرتبط
مهندسی و علوم پایه سایر رشته های مهندسی مهندسی (عمومی)
پیش نمایش صفحه اول مقاله
Weldability of Al4C3–Al composites via diffusion welding technique
چکیده انگلیسی

In this study, Al–Al4C3 composites, produced by powder metallurgy in situ techniques, were joined by diffusion welding technique at 250 MPa pressure with various welding temperatures and durations. Microstructures and shear strengths of the joined areas were determined. Al powders were mixed with 2% carbon black and milled in a high energy ball mill (mechanical alloying) for up to 20 h. In order to obtain cylindrical blanks with 10 mm in diameter and 15 mm in height, powders were compacted in a single action press at 1000 MPa. Samples were sintered in Ar atmosphere at 650 °C and metal matrix composite (MMC) containing 8% Al4C3 particles were produced. Products were then joined to each other by using diffusion welding techniques. Scanning electron microscopy examination was carried out on the welded interfaces and shear tests were conducted to the sample interfaces to find out the effect of welding temperatures and duration on the weldability properties. It was found that high welding temperatures resulted in increase of both joined strength and shear properties. However, increase in welding duration did not make any detectable changes. Results indicated that MMC could be joined by diffusion welding technique successfully with the 88% strength of base material.

ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Materials & Design - Volume 26, Issue 6, 2005, Pages 555–560
نویسندگان
, , , ,