Coupling effect of waste automotive engine oil in the preparation of wood reinforced LDPE plastic composites for panels

We demonstrated the formulation of wood plastic composite (WPC) materials with flexural strength of 13.69 ± 0.09 MPa for applications in outdoor fencing using municipal waste precursors like low density polyethylene (LDPE) plastics (54.0 wt. %), sawn wood dust with particle size between 64 and 500 μm derived from variable hardwood species (36.0 wt. %) and used automotive engine oil (10 wt. %). The WPC panels were prepared by pre-compounding, extruding at a screw auger torque of 79.8 Nm and pressing through a rectangular mould of dimension 132 mm × 37 mm × 5 mm at temperature 150 °C. The efficacy of black waste oil, as a coupling agent, was demonstrated by the absence of voids and pull-outs on microscopic examination using scanning electron microscopy. No hazardous substances were exhaled during thermo-gravimetric mass spectrometry analysis. The percentage crystallinity of the LDPE in the as-prepared material determined by differential scanning calorimetry was 11.3%.