Hydrogen assisted cracking of high-strength weldable steels in sea-water

For fatigue test uniaxial tension loading under strain control (R = 0, Δɛ = 0.2-8%) was carried out at frequency 0.1 s−1. Reduction of time to failure was a measure of hydrogen degradation. Fracture modes were investigated with the use of a scanning electron microscope (SEM).