Microstructure evolution and room temperature fracture toughness of directionally solidified NiAl-31Cr3Mo-0.2Si near-eutectic alloy at different withdrawal rates
Keywords: NiAl intermetallics; Directional solidification; Microstructure; Fracture toughness;