In-plane and through-plane non-uniform carbon corrosion of polymer electrolyte fuel cell cathode catalyst layer during extended potential cycles
Keywords: سلول سوختی الکترولیت پلیمر (PEFC); Polymer electrolyte fuel cell (PEFC); Potential cycling; Carbon corrosion; Focused ion beam (FIB)/scanning electron microscope (SEM); Pore-filling; Image analysis;