عنوان انگلیسی مقاله ISI
Comparison of small and long fatigue crack growth behavior in AA 7050-T7451
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
7050-T7451 aluminum alloyLong crackThreshold - آستانهFatigue crack propagation - انتشار ترک خستگیCrack closure - بستن تکه تکهShort crack - ترک کوتاهsmall crack - ترک کوچکMicrostructure - ساختار(بافت) ذره ای و کوچکStress intensity factor - فاکتور شدت تنشMicrostructural barrier - مانع میکرو سازمانیcrack growth rate - نرخ رشد ترک
موضوعات مرتبط
مهندسی و علوم پایه
سایر رشته های مهندسی
مهندسی مکانیک
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Comparison of small and long fatigue crack growth behavior in AA 7050-T7451 Comparison of small and long fatigue crack growth behavior in AA 7050-T7451](/preview/png/10152369.png)
چکیده انگلیسی
Fatigue crack growth behaviors of small and long cracks are compared in terms of crack closure, from near-threshold to final fracture, in over-aged aluminum alloy AA 7050-T7451. This is done experimentally to quantify inputs for crack propagation models such as the Navarro-Rios model. Growth rate of small cracks are determined as a function of stress intensity factor range using replicas taken from etched specimens loaded at high and low stress amplitudes. Similar data for long cracks are obtained using a compact tension C(T) specimen. Recrystallized grains are found to be the most significant microstructural barrier to propagation when cracks are small. In addition, small cracks typically appear to behave as closure-free long cracks. Transition from apparent closure-free to crack closure behavior is observed and characterized in terms of grain size. Finally, analysis of crack closure effects on C(T) specimens shows that long cracks propagating in the studied aluminum undergoes roughness- and oxide-induced closure.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Engineering Fracture Mechanics - Volume 202, 15 October 2018, Pages 20-32
Journal: Engineering Fracture Mechanics - Volume 202, 15 October 2018, Pages 20-32
نویسندگان
C. Bianchetti, R. Zheng, R.R. Chromik, M. Lévesque, M. Brochu,