Spark plasma sintering reaction synthesized TiB reinforced titanium matrix composites

The in situ TiB particle reinforced titanium metal matrix composites were prepared using MA followed by park plasma sintering (SPS) with a heating rate of 50 °C/min. The in situ TiB were synthesized by chemical reaction between TiB2 and Ti during the SPS process. The microstructure of the composites sintered at 800, 1000 and 1200 °C were investigated. TiB whiskers are needle-shape and uniformly dispersed in the titanium matrix. The interface between the in situ TiB needles and the titanium matrix is singular and faceted. The composite sintered at 1000 °C has a maximum value of relative density of 99.6%, and good mechanical properties with a flexural strength of 1007 MPa, Young's modulus of 146 GPa and fracture toughness of 8.64 MPa·m1/2, respectively. The fractographs of all composites exhibit a predominantly brittle cleavage fracture mechanism. The elastic modulus of synthesized TiB was estimated.