Neutron diffraction studies on lattice strain evolution around a crack-tip during tensile loading and unloading cycles

Elastic lattice-strain profiles ahead of a fatigue-crack-tip were measured during tensile loading and unloading cycles using neutron diffraction. The crack-closure phenomenon after an overload was observed. Furthermore, the plastic-zone size in front of the crack-tip was estimated from the diffraction-peak broadening, which showed good agreement with the calculated result.