Phase transformations and phase stability of the AlCuFe alloys with low-Fe content
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Phase transformations and phase stability of the AlCuFe alloys with low-Fe content Phase transformations and phase stability of the AlCuFe alloys with low-Fe content](/preview/png/10655780.png)
چکیده انگلیسی
Phase transformation and microstructure of the AlCuFe alloys of the approximate compositional range of 20-50 at.% Cu and 1-10 Fe at.% have been investigated for annealed samples by means of differential thermal analysis, magneto-thermal analysis, scanning electron microscopy, electron probe analysis and powder X-ray diffraction. Representative phase transformations categorized as polymorphic, discontinuous precipitation, quasi-binary eutectoid, and ternary transition reaction (U-type) phase transformation are presented. These phase transformations are found to have a common feature, which is characterized by a dissolution of a primitive CsCl-type cubic phase and a formation of a face-centered orthorhombic phase. The crystal structures of the cubic and orthorhombic phases are determined from the powder diffraction data using routines for indexing DICVOL, for intensity extraction and ab initio structure determination EXPO and for Rietveld refinement FULPROF. A face-centered orthorhombic cell (a=8.1530(3), b=14.1370(4), c=10.0736(4), Vol=1161.0(7), Z=4, at room temperature) with a starting structural model of ζ1-Al3Cu4 (space group Fmm2, Z=4) approximates the observed pattern of powder sample quenched from 620 °C fairly well. Refined orthorhombic cell dimensions are obtained by in situ high-temperature X-ray diffraction at 463, 553 and 636 °C. These phase transformations are sensitive to the heat treatment and the alloy composition. They can be suppressed at moderate cooling rates. The metastable structures for both slowly cooled and as-cast alloys are found to contain the cubic phase replacing the equilibrium orthorhombic phase.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Intermetallics - Volume 13, Issue 11, November 2005, Pages 1195-1206
Journal: Intermetallics - Volume 13, Issue 11, November 2005, Pages 1195-1206
نویسندگان
Liming Zhang, Julius Schneider, Reinhard Lück,