Mechanical properties and oxidation behaviour of two-phase iron aluminium alloys with Zr(Fe,Al)2 Laves phase or Zr(Fe,Al)12 Ï1 phase
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
A. Iron aluminides (based on FeAl) - A. آلومینید آهن (بر اساس FeAl)B. Oxidation - B. اکسیداسیونB. Brittleness and ductility - B. بی تابی و انعطاف پذیریB. Yield stress - B. تنش تولیدB. Mechanical properties at high temperatures - B. خواص مکانیکی در دماهای بالاB. Mechanical properties at ambient temperature - B. خواص مکانیکی در دمای محیط
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
![عکس صفحه اول مقاله: Mechanical properties and oxidation behaviour of two-phase iron aluminium alloys with Zr(Fe,Al)2 Laves phase or Zr(Fe,Al)12 Ï1 phase Mechanical properties and oxidation behaviour of two-phase iron aluminium alloys with Zr(Fe,Al)2 Laves phase or Zr(Fe,Al)12 Ï1 phase](/preview/png/10655888.png)
چکیده انگلیسی
Two-phase Fe-rich Fe-Al-Zr alloys have been prepared consisting of binary Fe-Al with a very low solubility for Zr and the ternary Laves phase Zr(Fe,Al)2 or Ï1 phase Zr(Fe,Al)12. Yield stress, flexural fracture strain, and oxidation behaviour of these alloys have been studied in the temperature range between room temperature and 1200 °C. Both the Laves phase and the Ï1 phase act as strengthening phases increasing significantly the yield stress as well as the brittle-to-ductile transition temperature. Alloys containing disordered A2+ ordered D03 Fe-Al show strongly increased yield stresses compared to alloys with only A2 or D03 Fe-Al. The binary and ternary alloys with about 40at.% Al and 0 or 0.8at.% Zr show the effect of vacancy hardening at low temperatures which can be eliminated by heat treatments at 400 °C. At higher Zr contents this effect is lost and instead an increase of low-temperature strength is observed after the heat treatment. The increase of the high-temperature yield strength of Fe-40at.% Al by adding Zr is much stronger than by other ternary additions such as Ti, Nb, or Mo. Tests on the oxidation resistance at temperatures up to 1200 °C indicate a detrimental effect of Zr already for additions of 0.1at.%.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Intermetallics - Volume 13, Issue 12, December 2005, Pages 1275-1285
Journal: Intermetallics - Volume 13, Issue 12, December 2005, Pages 1275-1285
نویسندگان
F. Stein, M. Palm, G. Sauthoff,