Metal-organic framework derived magnetic nanoporous carbon as an adsorbent for the magnetic solid-phase extraction of chlorophenols from mushroom sample

In this work, a metal-organic framework derived nanoporous carbon (MOF-5-C) was fabricated and modified with Fe3O4 magnetic nanoparticles. The resulting magnetic MOF-5-derived porous carbon (Fe3O4@MOF-5-C) was then used for the magnetic solid-phase extraction of chlorophenols (CPs) from mushroom samples prior to high performance liquid chromatography–ultraviolet detection. Scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and N2 adsorption were used to characterize the adsorbent. After experimental optimization, the amount of the adsorbent was chosen as 8.0 mg, extraction time as 10 min, sample volume as 50 mL, desorption solvent as 0.4 mL (0.2 mL × 2) of alkaline methanol, and sample pH as 6. Under the above optimized conditions, good linearity for the analytes was obtained in the range of 0.8–100.0 ng g−1 with the correlation coefficients between 0.9923 and 0.9963. The limits of detection (S/N = 3) were in the range of 0.25–0.30 ng g−1, and the relative standard deviations were below 6.8%. The result showed that the Fe3O4@MOF-5-C has an excellent adsorption capacity for the analytes.

A magnetic nanoporous carbon Fe3O4@MOF-5-C was prepared as the MSPE adsorbent for the extraction of some chlorophenols from mushroom samples.Figure optionsDownload as PowerPoint slide