Synthetic LiFePO4/C without using inert gas

LiFePO4/C was synthesized by high temperature solid-state method with cheap Fe2O3, LiH2PO4 and glucose as raw materials in absence of inert gas. The sample had ordered olivine-type structure other impurities characterized by the test of X-ray diffraction (XRD). The charge-discharge test showed the sample could demonstrate 120.5 mAh/g at 0.2C rate with good cyclic capability. The powder microelectrode cyclic voltammetry test indicated that the redox process of the sample had good reversibility.