![عکس صفحه اول مقاله: Multihydroxylated aryl amine as a novel alcohol-processable hole-transport molecular glass exhibiting remarkable resistance to weakly polar solvents Multihydroxylated aryl amine as a novel alcohol-processable hole-transport molecular glass exhibiting remarkable resistance to weakly polar solvents](/preview/png/1265223.png)
• The synthesis of a multihydroxylated small-molecule aryl amine was presented.
• The compound shows a contrasting solubility in polar and weakly polar solvents.
• It was used as an alcohol-processed hole-transport layer in bottom-anode OLEDs.
Multihydroxylation of a small-molecule aryl amine leads to a contrasting solubility in polar and weakly polar solvents. The resulting compound shows an intrinsic amorphous morphology with a high Tg of 190 °C and is capable of affording uniform smooth and transparent films, spin-cast from 2-propanol. The fitting of the space-charge-limited current characteristics reveals a hole mobility of ∼4.6 × 10−6 cm2 V−1 s−1 at low-voltages. Incorporating this new compound as a hole-transport layer into conventional bottom-anode organic light-emitting diodes that consisted of a solution-processed emitter provides promising performance.
Alcohol-processable hole-transporting molecular glass.Figure optionsDownload as PowerPoint slide
Journal: Organic Electronics - Volume 14, Issue 8, August 2013, Pages 2051–2057