cis-[Ni(μ-ox)(H2O)2]∞: Metal organic coordination polymer assembled by oxalate ligand: Structural and magnetic characterization

In this work, we describe for first time, the structure and magnetic characterization of the one dimensional catena cis-[Ni(μ-ox)(H2O)2]∞ (1), which was obtained by solvothermal synthesis. Cis-[Ni(μ-ox)(H2O)2]∞ crystallizes in a C2/c spatial group. The asymmetric unit contains only one type of nickel atom, oxalate ligand and water molecules. The chain backbone is constructed by the bis-chelating coordination mode of the oxalate ligand, presenting a zigzag chain in the [1 0 1] direction. The nickel ions have a distorted octahedral geometry, surrounded by six oxygens, four of them from two different oxalate ligands and the other two from the cis-coordinated water molecules. Thermal dependence of the magnetic susceptibility of (1) was studied in a temperature range of 2.5–255 K, at applied fields of 0.10 and 0.25 kOe. The plot of χMT(T) shows antiferromagnetic interactions between the Ni(II) centres. The experimental data were fitted between 255 and 30 K, using an empirical expression for a chain of equally spaced Ni(II) centres. The best fit of the experimental date gave a J value of −57 cm−1, which is much higher that the obtained for the trans-analogue. Irreversibility between ZFC and FC measurements below 9 K was observed, indicating some kind of magnetic ordering.

In this work, we describe the structure and magnetic characterization of the one dimensional catena cis-[Ni(μ-ox)(H2O)2]∞. The chain backbone is constructed by the bis-chelating coordination mode of the oxalate ligand, presenting a zigzag chain in the [1 0 1] direction. Thermal dependence of the magnetic susceptibility was studied in a temperature range of 2.5–255 K, at applied fields of 0.10 and 0.25 kOe. The plot of χMT(T) shows antiferromagnetic interactions between the Ni(II) centres and the irreversibility between ZFC and FC measurements below 9 K indicate some kind of magnetic ordering.Figure optionsDownload as PowerPoint slideHighlights
► Structural and magnetic characterization of the one dimensional catena cis-[Ni(μ-ox)(H2O)2]∞.
► The zigzag chain backbone is constructed by bis-chelating coordination mode of the oxalate ligand.
► Magnetic coupling of the Ni(II) ions through the oxalate bridges are antiferromagnetics.
► Irreversibility between ZFC and FC measurements was observed, indicating a magnetic ordering.