Synthesis, photoluminescent and electroluminescent properties of a novel europium(III) complex involving both hole- and electron-transporting functional groups

A novel europium(III) complex involving a carbazole fragment as hole-transporting group and an oxadiazole fragment as electron-transporting group was synthesized and used as red light-emitting material in organic light-emitting diodes (OLEDs). The complex is amorphous, and exhibits high glass transition temperature (Tg = 157 °C) and high thermal stability with a 5% weight loss temperature of 367 °C. Two devices, device 1: ITO/NPB (40 nm)/Eu(III) complex (30 nm)/Alq3 (30 nm)/LiF (1 nm)/Al (100 nm) and device 2: ITO/NPB (40 nm)/3% Eu(III) complex: CBP (30 nm)/BCP (10 nm)/Alq3 (30 nm)/LiF (1 nm)/Al (100 nm), were fabricated, where NPB is N,N′-di(naphthalene-1-yl)-N,N′-diphenyl-benzidine, Alq3 is tris(8-hydroxyquinoline) Al(III), CBP is 4,4′-bis(carbazole-9-yl)-biphenyl, and BCP is 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline, respectively. In contrast with device 1, owing to less self-quenching and better charge confinement, device 2 shows improved performances: the maximum luminance of device 2 was dramatically increased from 199 to 1845 cd/m2, the maximum current efficiency was increased from 0.69 to 2.62 cd/A, the turn-on voltage was decreased from 9.5 to 5.5 V, and higher color purity was attained.