Mechanically activated granulated blast furnace slag (GBFS) was used in the range of 50–95% to replace clinker in portland slag cement (PSC). The slag and clinker were activated separately using an attrition mill and mixed to prepare cement formulations. Use of activated slag resulted in a remarkable increase in strength vis-à-vis commercial slag cement. Both 1-day and 28-day strength were found to increase with an increase in slag content up to 70%. The strength of the sample containing 80–85% slag was comparable to the commercial cement used as a reference. It was observed that mechanical activation of slag was more critical from the point of view of strength development. The hydrated cement samples were characterised using powder X-ray diffraction (XRD), scanning electron microscopy with X-ray microanalysis (SEM-EDS) and simultaneous thermogravimetry and differential thermal analysis (TG/DTA). It is established that microstructural changes resulting from enhanced reactivity of slag and densification are related with the improvement in cement strength.
Journal: Cement and Concrete Composites - Volume 30, Issue 8, September 2008, Pages 679–685