Some factors affecting delayed ettringite formation in heat-cured mortars

Although more than 10 years of studies on delayed ettringite formation (DEF) have led to consensus in numerous areas of past disagreements, some questions remain experimental work is needed to complete the knowledge of this pathology. Following this objective, this paper studies the influence of pre-existing microcracking, wetting/drying cycles and the type of sulfated addition on DEF in steam cured mortars. The mortar specimens were prepared using an Ordinary Portland Cement and two types of sulfate were added to the mixtures: calcium sulfate (CaSO4) or sodium sulfate (Na2SO4). The results confirm the well-known effect of temperature: no expansion was observed in any of the mixtures cured at room temperature. Moreover, no expansion was observed after 800 days for the reference mortar or for the mortar containing calcium sulfate but all the specimens of heat-cured mortars containing sodium sulfate expanded markedly after about 50 days whatever the supplementary treatments applied (thermal shrinkage or wetting/drying cycles). These results show the significant role played by alkalis in the occurrence of delayed ettringite. The supplementary treatments intended to cause prelimiray microcracking of the specimens did not promote expansion but contributed to a slight acceleration of the reaction. The ultimate values of expansion were similar to those obtained with sound mortars.