The ceramic dispersions were prepared using 0.85, 1.70, 4.25, 12.75 or 21.25 wt.% of monochloroacetic, dichloroacetic or trichoroacetic acid, 15 wt.% alumina and 2-propanol. The mechanism of anionic stabilization in 2-propanolic media was described. Alumina green bodies were prepared from the stable dispersion via electrophoretic deposition (EPD). It was found that increasing dispersion conductivity significantly influenced the EPD yields. The most effective electrophoretic depositions were performed from dispersions with conductivity in range 4.0–5.3 × 10−4 S m−1. Deposits with the highest green density were prepared from the dispersion stabilized by trichloroacetic acid. This behavior was explained by low voltage drop during deposition. The surface roughness was high at low dispersion conductivity and with increasing acid concentration in dispersion the surface of deposits was smoother. The mechanism of particle arrangement in deposit was discussed. Influence of stabilizer amount in the dispersion on the hardness and fracture toughness was described.
Journal: Journal of the European Ceramic Society - Volume 34, Issue 14, November 2014, Pages 3365–3371