Structural determination and microwave properties of (x)Re(Co1/2Ti1/2)O3-(1 â x)CaTiO3 (Re = La and Nd) solid solutions
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله

چکیده انگلیسی
Solid solutions of (x)Re(Co1/2Ti1/2)O3-(1 â x)CaTiO3 (Re = La and Nd, abbreviated to xLCT and xNCT, respectively) where x = 0, 0.25, 0.5, 0.75 and 1 have been fabricated using solid state synthesis. Samples have been examined using X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy (TEM) and their dielectric properties measured at microwave (MW) frequencies. Formation of single phase solid solutions were confirmed by XRD and the measured lattice parameters varied linearly from LCT (a = 5.66 Ã
, b = 7.867 Ã
and c = 5.494 Ã
) and NCT (a = 5.636 Ã
, b = 7.914 Ã
and c = 5.461 Ã
) to CT (a = 5.596 Ã
, b = 7.731 Ã
and c = 5.424 Ã
). XRD and TEM confirmed both in-phase and antiphase rotations of O-octahedra consistent with an aâaâc+ tilt system across the entire solid solution series. Electron diffraction revealed that LCT and NCT have reflections associated with B-site cation ordering which is absent for x â¤Â 0.75. MW dielectric measurements showed that LCT and NCT were highly insulating with microwave quality factor (Qf0) values of 39,000 and 34,000, respectively. Compositions anticipated to have a zero temperature coefficient of resonant frequency (Ïf) are 0.48LCT-CT and 0.52NCT-CT with Ér = 45 and Qf0 â¼Â 5000 and Ér = 43 and Qf0 â¼Â 4000, respectively.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 26, Issue 6, 2006, Pages 875-882
Journal: Journal of the European Ceramic Society - Volume 26, Issue 6, 2006, Pages 875-882
نویسندگان
D.L. Cairns, I.M. Reaney, N. Otten, D. Iddles, T. Price,