![عکس صفحه اول مقاله: Preparation and luminescent properties of orange reddish emitting phosphor LaMgAl11O19:Sm3+ Preparation and luminescent properties of orange reddish emitting phosphor LaMgAl11O19:Sm3+](/preview/png/1494134.png)
• LaMgAl11O19:Sm3+ phosphors were synthesized at 1600 °C for 4 h.
• The phosphors present an orange reddish emission under 403 nm excitation.
• The d–d interactions result in the concentration quenching with 5 mol% Sm3+ added.
• The LaMgAl11O19:Sm3+ phosphor presents a potential application in w-LEDs.
An orange reddish emitting phosphor, LaMgAl11O19:Sm3+, was synthesized by a high temperature solid-state reaction, and the phase formation, crystal structure and luminescence properties were investigated respectively. The LaMgAl11O19:Sm3+ phosphor presents a highly intense orange reddish emission peak under the near ultraviolet excitation at 403 nm, which is corresponds to the 4G5/2 → 6HJ (J = 5/2, 7/2, 9/2 and 11/2) transitions of Sm3+ ions. It was found that the dipole–dipole interactions mainly results in the concentration quenching in the LaMgAl11O19:Sm3+ phosphor with a critical quenching concentration at about 5 mol%. The temperature dependence of luminescence properties was studied from 25 to 200 °C and indicated that LaMgAl11O19:0.05Sm3+ phosphors had a relatively higher quenching temperature. The chromatic properties of LaMgAl11O19:0.05Sm3+ phosphor have been found to have chromaticity coordinate of (0.578, 0.420). All these properties indicate that the orange reddish emitting LaMgAl11O19:Sm3+ phosphor has a potential application in w-LEDs.
Journal: Optical Materials - Volume 37, November 2014, Pages 110–114