Elevated-temperature impact toughness of Mg–(Gd, Y)–Zr alloy

 The Charpy impact results for Mg–10Gd–3Y–0.5Zr and Mg–11Y–5Gd–2Zn–0.5Zr alloys at various temperatures showed that Mg–10Gd–3Y–0.5Zr was more sensitive to temperature. The increase in impact toughness with temperature was related to the blunt crack-tip at high temperatures. The delamination and local melt of matrix were responsible for the brittle-to-ductile transition of GW103 alloy. The branch and bridging of cracks resulting from ordered phases played an import role in the change in fracture mode from cleavage fracture to quasi-cleavage and dimple-fracture for WGZ1152 alloy.